GNEE STEEL se yon founisè asye pwofesyonèl. GNEE Global Enterprises kanpe wo ak yon anprint entènasyonal enpresyonan, ekspòte pwodwi li yo nan plis pase 70 peyi ak rejyon yo. Soti nan Etazini rive nan Inyon Ewopeyen an, pwodwi nou yo te genyen yon gwo repitasyon pou bon jan kalite eksepsyonèl yo ak sèvis yo. Nou fyè dèske nou te etabli tèt nou kòm yon jwè mondyal serye nan endistri nou an.
Rechèch sou rezistans tanperati ki ba nan plak ki reziste
Mete ki reziste plak se asye ki pi komen yo itilize nan machin jeni. Asye sa a mande pou bon rezistans ba-tanperati ak soudabilite anba dite segondè. Atik sa a premye itilize etid la eksperimantal nan severite enpak anba yon seri de tanperati, paske li se relativman fasil mezire endèks la enèji materyèl ak rezilta tès yo relativman rich ak matirite. Sepandan, endèks severite enpak la toujou difisil pou bay yon evalyasyon efikas nan sekirite. Nan sans sa a, papye sa a sèvi ak yon tès dinamik chire (DT) tou pre gwosè aktyèl la pou plis etidye solidite ba-tanperati plak la ki reziste. Rezilta tès yo montre ke tou de enpak seri ak chire dinamik montre yon pi wo plato anwo ak pi ba tanperati tranzisyon ductile-frajil. , materyèl la gen bon rezistans tanperati ki ba.
Materyèl eksperimantal la se JFE-C400 plak ki reziste. Pwosesis pwodiksyon li se: konvètisè + raffinage LF deyò gwo founo dife a → depoze mwazi → woule cho → modulasyon (trempe + tanperaman). Epesè plak la se 4{{10}}mm, ak konpozisyon chimik la se (fraksyon mas, %): 0.10C, 0.28Si, 0.42Mn, 0.001S,<0.005P, 3.0Ni, 1.0Cr, 0.25Mo. Samples were taken transversely along the surface and center of the wear-resistant plate, and standard specimens were processed according to the provisions of GB/T228-2002 "Metal Materials Room Temperature Tensile Test Method", and conventional tensile and Z-direction tensile tests and a series of impact tests were conducted. According to GB/T5482-2007 "Metal Materials Dynamic Tear Test Method", samples were taken and processed into 180mm×40mm×16mm specimens for a series of dynamic tear tests. The opening direction of the specimens was perpendicular to the rolling direction. The metallographic structure and grain size were corroded by 4% nitric alcohol, saturated picric acid + a small amount of detergent respectively. The tensile fracture morphology was observed using S4300 scanning electron microscope.
Endistriyèl pwodwi plak ki reziste mete yo gen grenn amann ak estrikti inifòm. Plak ki reziste mete yo gen yon tanperati tranzisyon ki ba difisil-a-frajil ak bon tanperati ki ba-tanperati, ki garanti sekirite nan machin jeni. Nan metòd rechèch la nan severite tanperati ki ba, li jwenn ke gwo-echèl tès dinamik chire ka plis revele karakteristik sa yo nan tranzisyon ductile-frajil.